공급 업체와 통신? 공급 업체
Jason Song Mr. Jason Song
나는 당신을 위해 무엇을 할 수 있습니까?
지금 채팅 공급 업체에 문의하십시오
He Bei GuangHao Pipe Fittings Co .,LTD (Cangzhou Sailing Steel Pipe Co., Ltd)

He Bei GuangHao Pipe Fittings Co .,LTD (Cangzhou Sailing Steel Pipe Co., Ltd)

sales@ghsailingpipe.com

86-18632722111

He Bei GuangHao Pipe Fittings Co .,LTD (Cangzhou Sailing Steel Pipe Co., Ltd)
He Bei GuangHao Pipe Fittings Co .,LTD (Cangzhou Sailing Steel Pipe Co., Ltd)
I agree Bossgoo.com will authorize the transaction payment on Bossgoomall.com. Bossgoomall.com is a subsidiary of Bossgoo.com group, Please rest assured to trade.
I agree
제품 리스트쇠 파이프이음매없는 파이프ASTM A333GR3 이음매없는 강관

ASTM A333GR3 이음매없는 강관

Payment Type:
L/C,T/T,D/P,Paypal,Money Gram,Western Union
Incoterm:
FOB,CFR,CIF,FCA,CPT
Min. Order:
1 Piece/Pieces
Delivery Time:
25 Days
Transportation:
Ocean,Land,Air
Port:
Tianjin,Qingdao,Shanghai
  • 제품 설명
Overview
Product Attributes

모형1/2-124" SEAMLESS

상표GH

Supply Ability & Additional Informations

포장나무로되는 케이스 .wooden 깔판, 또는 고객 요구에 관해서는

생산력50000 Tons

수송Ocean,Land,Air

원산지중국

공급 능력50000 Tons

인증 IS0/API/PED/QTY/CE

HS 코드7304319000

포트Tianjin,Qingdao,Shanghai

지불 유형L/C,T/T,D/P,Paypal,Money Gram,Western Union

IncotermFOB,CFR,CIF,FCA,CPT

배송 시간25 일

Packaging & Delivery
Selling Units:
Piece/Pieces
Package Type:
나무로되는 케이스 .wooden 깔판, 또는 고객 요구에 관해서는


1597669927

저온 서비스를 위한 ASTM A333 등급 3 이음매없는 파이프

ASTM A333 (ASME S / A-333) 파이프 등급은 저온 서비스를 허용합니다. 이 사양은 거의 독점적으로 이음매없는 공칭 (평균) 벽 파이프를 다룹니다. 여러 등급의 페라이트 강이 포함됩니다. 벽 두께가 두꺼울수록 저온 충격 특성에 악영향을 미치기 때문에 일부 제품 크기는이 사양에서 사용할 수 없습니다. A333 파이프는 1, 3, 4, 6, 7, 8, 9, 10, 11 번으로 지정된 9 가지 등급으로 제공됩니다.


A333 사양

ASTM A333 Gr 3, 저온, Stockist, 공급 업체 및 수출 업체

  • 강종 : ASTM A333 Grade 3
  • 길이 : 5000 mm-7000 mm, 10000 mm-12000 mm 또는 클라이언트 요구 사항에 따라.
  • 외경 : 1/2 "~ 42" -이음매없는
  • 외경 : 14 "~ 100" -용접
  • 벽 두께 : 2.00 mm ~ 100.00 mm
  • 배송 조건 : 최대 1 주일 (재고에서 모두)

범위

이 사양은 저온 및 노치 인성이 필요한 기타 응용 분야에서 사용하기위한 공칭 (평균) 벽 이음매없는 용접 탄소 및 합금 강관을 다룹니다. 나열된 바와 같이 여러 등급의 페라이트 강이 포함됩니다. 벽 두께가 두꺼울수록 충격 특성에 악영향을 미치기 때문에 일부 제품 크기는이 사양에 따라 제공되지 않을 수 있습니다.

SI 단위 또는 인치-파운드 단위로 표시된 값은 별도로 표준으로 간주됩니다. 텍스트 내에서 SI 단위는 괄호 안에 표시됩니다. 각 시스템에 명시된 값은 excat 등가물이 아닐 수 있습니다. 따라서 각 시스템은 서로 독립적으로 사용해야합니다. 두 시스템의 값을 결합하면 표준과 일치하지 않을 수 있습니다.

열처리

모든 이음매없는 용접 파이프는 다음 방법으로 미세 구조를 제어하도록 처리되어야합니다. A 333 / A 333M-05 섹션 4.2.1.1에 따라 정규화; 섹션 4.2.1.2 또는 섹션 4.2.1.3 A 333 / A 333M – 05에 따라 담금질 및 템퍼링 섹션 4.2.2.1 A 333 / A 333M – 05 섹션 4.2.2.2에 따라 이중 정규화 및 템퍼링

화학적 구성 요소

Element
Grade 3
Carbon, max 0.19
Manganese 0.31-0.64
Phosphorus, max 0.025
Sulphur, max 0.025
Silicon 0.18-0.37
Nickel 3.18-3.82
Chromium --
Copper --
Aluminum --
Vanadium, max --
Columbium, max --
Molybdenum, max --

0.30 % 미만의 0.01 % 탄소 감소에 대해 1.06 % 이상의 0.05 % 망간 증가는 최대 1.35 % 망간까지 허용됩니다.

인장 요구 사항

 
Grade 3
 
psi
MPa
Tensile strength Min
65 000
450
Yield strength Min
35 000
240
  Longitudinal Transverse
Elongation in 2 in or 50 mm (or 4D), min, %    
Basic minimum elongation for walls 5/16 in. [8mm] and over in thickness, strip tests, and for all small sizes tested in full section. 30 20
When standard round 2-in, or 50-mm gage length or proportionally smaller size test specimen with the gage length equal to 4D (4 times the diameter) is used 22 14
For strip tests, a deduction for each 1/32 in [0.8 mm] decrease in wall thickness below 5/16 in [8 mm] from the basic minimum elongation of the following percentage 1.50 1.00

2 인치 또는 50mm 신장, 최소, %

Wall Thickness
Grade 3
in
mm
Longitudinal
Transverse
5/16 (0.312) 8 30 20
9/32 (0.281) 7.2 28 19
1/4 (0.250) 6.4 27 18
7/32 (0.219) 5.6 26 --
3/16 (0.188) 4.8 24 --
5/32 (0.156) 4 22 --
1/8 (0.125) 3.2 21 --
3/32 (0.094) 2.4 20 --
1/16 (0.062) 1.6 18 --

영향 요구 사항

Size of Specimen
Minimum Average Notched Bar Impact Value of Each Set of Three Specimen
Minimum Notched Bar Impact Value of One Specimen only a Set
 
ft-lbf
J
ft-lbf
J
10 by 10 13 18 10 14
10 by 7.5 10 14 8 11
10 by 6.67 9 12 7 9
10 by 5 7 9 5 7
10 by 3.33 5 7 3 4
10 by 2.5 4 5 3 4
Straight line interpolation for intermediate values is permitted.
충격 온도
Grade
Minimum Impact Test Temperature
°F
°C
1
-50
-45
3
-150
-100
4
-150
-100
6
-50
-45
7
-100
-75
8
-320
-195
9
-100
-75
10
-75
-60
11
-320
-195

기계적 테스트

가로 또는 세로 인장 시험 및 평탄화 시험, 경도 시험 또는 굽힘 시험 배치 식로에서 열처리 된 재료의 경우 각 처리 된 로트에서 파이프의 5 %에 ​​대해 시험을 실시해야합니다. 작은 로트의 경우 적어도 하나의 파이프를 테스트해야합니다. 연속 공정으로 열처리 된 재료의 경우, 로트의 5 %를 구성 할 수있는 충분한 수의 파이프에서 테스트를 수행해야합니다. 수압 시험 충격 시험 완성 된 파이프에서 채취 한 시험편에 대한 열처리 하중으로 재현 된 각 열로 3 개의 시험편을 파괴하는 것으로 구성된 노치 바 충격 시험을 1 회 실시해야합니다.

열처리 요건

모든 이음매없는 용접 파이프는 다음 방법으로 미세 구조를 제어하도록 처리되어야합니다. A 333 / A 333M-05 섹션 4.2.1.1에 따라 정규화; 섹션 4.2.1.2 또는 섹션 4.2.1.3 A 333 / A 333M – 05에 따라 담금질 및 템퍼링 섹션 4.2.2.1 A 333 / A 333M – 05 섹션 4.2.2.2에 따라 이중 정규화 및 템퍼링

충격 온도 감소

Specimen Width Along Notch or Actual Material Thickness
Temperature Reduction , Degrees Colder
in
mm
°F
°C
0.394 10 (standard size) 0 0
0.354 9 0 0
0.315 8 0 0
0.295 7.5 (3/4 std. size) 5 3
0.276 7 8 4
0.262 6.67 (2/3 std. size) 10 5
0.236 6 15 8
0.197 5 (1/2 std. size) 20 11
0.158 4 30 17
0.131 3.33 (1/3 std. size.) 35 19
0.118 3 40 22
0.099 2.5 (1/4 std. size) 50 28
Straight line interpolation for intermediate values is permitted.